Product

Performance

Metal Fluorocarbon Painting Decorative Insulation
Board

Decoration
Layer

Multicolor Coating Decorative board

Super energy saved; high anti-cracking ; efficient simulation ;short construction period; super self-cleaning function, super-resistant scrub

Multicolor Coating , also known as liquid granite paint, is a high technology product with pure water, no pollution, rich granitic textures and polymer element structure. Compared with natural mineral paint, granite stone paint, texture paint, Sandstone paint and other sand sandstone,it has a completely different concept in nature.

Insulation Layer

EPS insulation layer
(Grade B1)

Heat conductivity ≤0.041.  volume-weight :18kg / m³ with the tensile strength:110--120kpa; volume-weight 20kg / m³ with the tensile strength :140kpa.

XPS insulation Layer
(Grade B1)

Heat conductivity ≤0.030. Volume-weight 25--45kg / m³ & tensile ≥150kpa. Strong compressive resistance.   30-40 years average using life. Excenllent structure load-bearing performance .

Polyurethane insulation board
(Grade B1)

Hard polyurethane with low thermal conductivity, good thermal performance. When the hard polyurethane with the  density of  35 ~ 40kg / m3, thermal conductivity is only 0.018 ~ 0.024w / (m.k), equivalent to  half of the EPS, is the lowest heat conductivity of all the insulation materials .

TPS insulation board
(Grade B1)

Heat insulation thermal conductivity is 0.060W / (m · k) ,it has good tensile compressive strength , impact resistance and stability ; its compressive strength reaches 150-500KPa

Rock wool  (Grade A)

Appearance quality: smooth surface, without prejudice practical scars, stains damaged. Combustion performance: non-combustible. Thermal load contraction temperature: 643 degrees.
Moisture absorption: 3.9%. Organic content: 2.9%.
Rockwool board basic parameters:
Apparent density: Rockwool 120 (kg / m3) ;Heat conductivity: 0.04 (W / (m.K))
Max operating temperature: 80 () ;Specifications: 950,1150 (mm )
Operation standard: GB;Operating temperature: 80 ()

Phenolic Foam Board(Grade B Grade A)

Not be melt at high temperatures ,not be softened, with low smoke, non-proliferation flame resistance, flame penetration, There is  no distortion, no burning ,no fire, being placed 10 minutes at 1400 , can effectively prevent the flames and smoke spread

        Test Item

Detection standard and requirements

The third party test results

 
Dimensional Deviation

Length(mm)

 
 
GB/T7748-1999

±1.5

-1.0~0

Width(mm)

±1.5

-1.0~0.5

Thickness(mm)

±0.5

-0.2~0.1

Diagonal difference(mm)

≤2.0

0.5

No straight degree in Border(mm/)

≤2.0

0

Warping degree(mm/m)

≤3.0

0

Test Item

Detection standard
and requirements

The third party test results

Coating thickness(μm)

GB/T13452.2-
2008-10

≥30

199

Coating adhesion(MPa)

GB/T5210-2006

≥0.3

1.7(0.8-2.7),100%A

Hardness(Pencil)

GB/T6739-2006

≥4H

6H No scraping damage

Abrasive resistance(750g/500r),
Suitable grinding wheel type:CS-10

GB/T1768-2006

0.003

Solvent resistance wiping(Butanone,
100times)

HC/T-3792-2005
Appendix

No undercasing

Meet the requirement

Acid-resistance(5%HC1 liquor,24H)

GB/T9274-1998

No blistering,No Falling off,non-discolouring

No Change

Alkali resistance

GB/T9274-1998

No blistering,No Falling off,non-discolouring

No Change

Abrasion performance

HC/T3793-2005-
4.1/4.3

≥5

12

Stain resistance

GB/T9757-2001
Appendix A

≤5

5

Scrub resistance

GB/T9266-2009

≥10000

>10000

Oil resistant(Immerse in engine oil  SE15W-40 24H)

GB/T9274-198888

No blistering,No Falling off,non-discolouring

No Change

Alkali burnout resistance(72H)

JG/T210-2007

No abnormalities

Salting-out resistance(144H)

JG/T210-2007

No abnormalities

Weather resistance

GB/T1865-2009,GB/T1766-2008

Artificial climate ageing and radiation exposure

4000Hrs after testing,Dulling≤3Grade,
Discoloration≤2Grade

Business Organizations

It is widely used in office building,hotel, High-end residential and other building’s decoration and insulation project.